1. Identificação | |
Tipo de Referência | Artigo em Revista Científica (Journal Article) |
Site | plutao.sid.inpe.br |
Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
Identificador | J8LNKAN8RW/34BEPQE |
Repositório | dpi.inpe.br/plutao@80/2008/12.04.12.03.03 (acesso restrito) |
Última Atualização | 2017:07.21.16.36.23 (UTC) marciana |
Repositório de Metadados | dpi.inpe.br/plutao@80/2008/12.04.12.03.04 |
Última Atualização dos Metadados | 2018:06.05.00.12.36 (UTC) administrator |
Chave Secundária | INPE--PRE/ |
DOI | 10.1166/jnn.2009.NS83 |
ISSN | 1533-4880 |
Rótulo | lattes: 3374288398505199 1 MirandaAzeBalBelFer:2008:NoPrOb |
Chave de Citação | MirandaAzeBalBelFer:2009:NoPrOb |
Título | A Novel Procedure to Obtain Nanocrystalline Diamond/Porous Silicon Composite by Chemical Vapor Deposition/Infiltration Processes |
Ano | 2009 |
Mês | June |
Data de Acesso | 18 maio 2024 |
Tipo Secundário | PRE PI |
Número de Arquivos | 1 |
Tamanho | 3376 KiB |
|
2. Contextualização | |
Autor | 1 Miranda, Claudia Renata Borges 2 Azevedo, Adriana Faria 3 Baldan, Maurício Ribeiro 4 Beloto, A F 5 Ferreira, Neidenêi Gomes |
Grupo | 1 2 3 LAS-CTE-INPE-MCT-BR |
Afiliação | 1 2 3 Instituto Nacional de Pesquisas Espaciais (INPE) |
Endereço de e-Mail do Autor | 1 claudia@las.inpe.br 2 3 baldan@las.inpe.br 4 5 neidenei@las.inpe.br |
Endereço de e-Mail | claudia@las.inpe.br |
Revista | Journal of Nanoscience and Nanotechnology |
Volume | 9 |
Número | 6 |
Páginas | 3877-3882 |
Nota Secundária | B2_BIOTECNOLOGIA B2_CIÊNCIAS_BIOLÓGICAS_II B2_CIÊNCIAS_BIOLÓGICAS_III A1_ENGENHARIAS_II A1_INTERDISCIPLINAR A2_MATERIAIS B1_MEDICINA_I B1_MEDICINA_II A2_MEDICINA_VETERINÁRIA B2_QUÍMICA |
Histórico (UTC) | 2008-12-04 16:12:39 :: lattes -> simone :: 2009-06-26 19:20:13 :: simone -> administrator :: 2010-05-12 02:04:01 :: administrator -> simone :: 2010-07-07 18:38:50 :: simone -> administrator :: 2013-09-24 21:56:16 :: administrator -> marciana :: 2009 2017-07-21 16:36:23 :: marciana -> administrator :: 2009 2018-06-05 00:12:36 :: administrator -> marciana :: 2009 |
|
3. Conteúdo e estrutura | |
É a matriz ou uma cópia? | é a matriz |
Estágio do Conteúdo | concluido |
Transferível | 1 |
Tipo do Conteúdo | External Contribution |
Tipo de Versão | publisher |
Palavras-Chave | Nanodiamond porous silicon Chemical Vapor Infiltration Chemical Vapor Depositation Acetonitrile |
Resumo | Nanocrystalline diamond (NCD) films were formed on porous silicon (PS) substrate by Chemical Vapor Deposition/Infiltration (CVD/CVI) process using a hot filament reactor. This innovative procedure is determinant to grow a controlled three-dimensional diamond structure with diamond grains formation in the pores, covering uniformly the different growth planes. In this CVI process, a piece of reticulated vitreous carbon (RVC) was used, under de PS substrate, as an additional solid source of hydrocarbon that ensures the production of pertinent carbon growth species directly on PS and into its pores. PS substrates were obtained by anodization etching process of n-type silicon wafer in a hydrofluoric acid (HF) solution containing acetonitrile (CH3CN) which result in an uniform and well controlled porous distribution and size when compared with the usual ethanol solution. Depositions were performed using Ar-H-2-CH4 where the methane concentration varied from 0 up to 1.0 vol%, to analyze the influence of RVC use as an additional carbon source on growth mechanism. Scanning Electron Microscopy (SEM) and Field Emission Gun (FEG) were used to investigate PS and NCD film morphology. SEM images of NCD showed faceted nanograins with average size from 5 to 16 nm and uniform surface texture covering all the supports among the pores resulting in an apparent micro honeycomb structure. Raman spectra confirmed the existence of sp(2)-bonded carbon at the grain boundaries. The spectra showed a peak that may be deconvoluted in two components at 1332 cm(-1) (diamond) and 1345 cm(-1) (D band). Two shoulders at 1150 and 1490 cm(-1) also appear and are assigned to transpolyacetylene (TPA) segments at the grain boundaries of NCD surfaces. In addition, X-ray diffraction analyses of all films presented characteristic diamond diffraction peaks corresponding to < 111 >, < 220 > and < 311 >. |
Área | FISMAT |
Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > A Novel Procedure... |
Conteúdo da Pasta doc | acessar |
Conteúdo da Pasta source | não têm arquivos |
Conteúdo da Pasta agreement | não têm arquivos |
|
4. Condições de acesso e uso | |
Idioma | en |
Grupo de Usuários | lattes simone administrator |
Grupo de Leitores | administrator marciana |
Visibilidade | shown |
Política de Arquivamento | denypublisher denyfinaldraft |
Permissão de Leitura | deny from all and allow from 150.163 |
Permissão de Atualização | não transferida |
|
5. Fontes relacionadas | |
Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 |
Acervo Hospedeiro | dpi.inpe.br/plutao@80/2008/08.19.15.01 |
|
6. Notas | |
Campos Vazios | alternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel dissemination format isbn lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project resumeid rightsholder schedulinginformation secondarydate session shorttitle sponsor subject targetfile tertiarymark tertiarytype typeofwork url |
|
7. Controle da descrição | |
e-Mail (login) | marciana |
atualizar | |
|